Y42CD4简介

Y42CD4,及该型号钢材的基本信息、化学元素成分、机械性能、力学性能、热处理温度、同等型号参照表等

Y42CD4

Y42CD4,及该型号钢材的基本信息、化学元素成分、机械性能、力学性能、热处理温度、同等型号参照表等

基本信息:
分类 种类 型号 标准 国家 应用
Steel Grades - Y42CD4
化学成分信息(mass fraction)(wt.%) of the Y42CD4
元素名称 最小值 最大值 近似值
Si 0.1000 0.4000 -
Mo 0.1500 0.3000 -
Mn 0.6000 0.9000 -
Cr 0.8500 1.1500 -
C 0.3900 0.4600 -
机械性能信息:
屈服强度Rp0.2(MPa) 抗拉强度Rm(MPa) 冲击率 伸长率 断面收缩率 热处理状态 布氏硬度(HBW)
179 (≥) 825 (≥) 31 11 43 Solution and Aging, Annealing, Ausaging, Q+T,etc 444
物理性质信息:
温度 弹性模量 系数 热导率 比热容量 比电阻率 密度 加权系数
31 - - 0.34 -
931 274 - 33.3 221 -
448 - 41 21.2 232 434
热处理信息:
Heat treated : 1529°C - 1112°C
对照表(同等等级)信息:
型号 标准 国家 应用
Y1Cr18Ni9 Improve the machinability, ablation resistance. Suitable for automatic lathe production of bolt and nut
1Cr18Ni9 High strength after cold forming, but elongation than 1 cr17ni7 slightly worse. Used in architectural decoration parts
1Cr18Mn10Ni5Mo3N Of urea with good corrosion resistance, can produce urea corrosion of the equipment.
1Cr17Ni7 High strength after cold forming. Used in railway vehicle, conveyor belt, bolt and nut, etc
Y1Cr18Ni9Se Improve the machinability, ablation resistance. Suitable for automatic lathe production of rivets, screws
0Cr18Ni9 Seamless stainless steel tubes for boiler and heat exchanger
00Cr19Ni10 Carbon content lower than 0Cr19ni9 steel, excellent intergranular corrosion resistance, is used for welding after the class is not processed parts
1Cr17Mn6Ni5N Nickel steel grade, instead of number 1 cr17ni7 and magnetism after cold working, used in railway vehicle, etc
1Cr18Mn8Ni5N Nickel steel, instead of 1cr18ni9
0Cr19Ni9N Based on 0cr19ni9 plus N, strength increase and the plastic is not down. Reduce the thickness of the material. As a structure with strength components
0Cr19Ni10NbN Based on zero cr19ni9 plus N and Nb, with better than 0 cr19ni9 properties and USES
00Cr18Ni10N In 00cr19ni10 adding N, on the basis of the above grades also features, use the same as the 0 cr19ni9n, but better intergranular corrosion resistance
1Cr18Ni12 Compared with 0 cr19ni9, processing low hardenability. Used for spinning processing, special drawing, cold heading
0Cr23Ni13 Corrosion resistance and heat resistance are better than 0cr19ni9
0Cr25Ni20 Oxidation resistance is better than 0cr23ni13. Mostly used as heat resistant steel
0Cr17Ni12Mo2 Seamless stainless steel tubes for boiler and heat exchanger
1Cr18Ni12Mo2Ti Seamless stainless steel tubes for boiler and heat exchanger
0Cr18Ni12Mo2Ti Seamless stainless steel tubes for boiler and heat exchanger
A-29 1025 General use carbon steel rod
1025 These products have been used typically for use in fabrication of fittings, but usage is not limited to such applications. These products are not typically used for deep forming or cupping operations.
标签: Y42CD4、Y42CD4钢材、Y42CD4材料
全球钢材百科网